杜邦氟橡胶GLT-600S推荐配方

跋锋寒

________________________________________________________________________________________
配方成分:        A10-01   A10-02    A10-03    A10-04             A10-05         A10-06
; R& Z/ r- N) [" X9 W_________________________________________________________________________________
Viton® GLT-600S 100      100       100        100                100            100

氧化锌            3        3          3          3                 3             3
6 o2 a, B% h, [, r
N990 (MT Black)  5        30          60

& n0 o( p* U" E$ B硅灰石              —        —           —        40                 —               —

6 u1 p( n( ]* {3 Q* x0 |0 l: vCaCO3            —        —           —        —                  40              —

BaSO4            —        —           —        —                   —            40

表面活性剂        0.5      0.5        0.5       0.5                0.5           0.5

, o# j' J5 m' T; KTAIC             3         3         3          3                 3              3

R.T.Vanderbilt
某交联剂          3        3          3          3                 3               3

! y: }% J2 u8 g* m7 bTotal phr =     114.5     139.5     169.5      149.5             149.5          149.5
+ X' N; L7 B+ t6 ^
Mooney Scorch at 121°C
Minimum, MU      23         31       43         33                37              27
2 pt rise (min)  15.9      9.3      6.5        13.7               10.7          15.7
5 pt rise (min)  17.1      10.8      8.2       14.9               11.5          16.5
10 pt rise (min) 18.8      12.1      9.8       15.8               12.2          17.5
0 g8 E! v8 ?- X  ~) ?
ODR at 162°C, 3° Arc, 100 Range, 30 Minute Clock
M-L (dam)        15       18        20          21                  24           19
ts-2 (min)       1.3      1.1       0.9         1.1                 1.1          1.4
t'50 (min)       2.4       2.4       2.4        2.4                 2.1          2.7
/ i4 s0 i& ^( z- W; ~t'90 (min)       6.9        7.1      8.8        5.2                 5.1          7.3
M-H (dam)         101       136      182        136                 137          120

MDR 2000 at 177°C, 0.5° Arc, 100 Range, 6 Minute Clock
( S8 {- P, C4 pM-L (dam)         1.4        2.1      3.3       2.3                 2.7           1.9
: `! h* M% T2 ~; h7 d' lts-2 (min)        0.5        0.4       0.3      0.4                 0.4           0.4
t'50 (min)        0.6        0.5       0.5      0.5                 0.5           0.6
' Z7 a9 g( ^8 o5 wt'90 (min)        0.9        1.0       1.3        0.8                 0.7         0.9


Physical Properties at R.T. — Original (Cure 5' at 177°C — no postcure)
& {; Q! L& _4 x3 `" F* YM-10, MPa         0.4         0.8        1.5      1.0                 0.6          0.7
% l0 s2 K! A* L$ \% D7 `M-100, MPa        1.2         3.2        6.7       7.0                2.1          1.6
# n9 q  @2 R+ E" H0 j. Q, GTensile, MPa      8.9         10.6      10.9       11.2               9.5           9.8
(T-B, psi)         (1286)     (1538)     (1575)    (1617)             (1372)       (1415)
Elongation, %      369        337        229         245               403           393
* `# I8 G0 T0 LHardness, A, pts    52        67         79          66               64              58

KRMQ

有参考意义，楼主辛苦了！

跋锋寒

有谁还在用这个配方的，我看了论坛的一些氟胶配方，有些区别啊。