请教HNBR配方设计问题

zhjlll1111

问问以下HNBR配方该如何设计啊，请高人指点。先谢谢了哦

Hardness (shore A)        70+/-5
Hardness (IRHD )       
Tensile (Mpa)         18 min
Ultimate Elongation (%)        290 min
6 e# ?6 e6 f( l2 W! bTear B,KN/m        35 min
Heat Resistance 160C@96hrs       
    Change in hardness (pts)        +12 max
& Y; `0 P7 C6 u5 l7 d3 j7 w    Change in tensile (%)        -18 max
" F, ^3 Z7 d7 d* ]7 T: X    Change in elongation (%)        -20 max
Oil Resistance 5W30 160C@504hrs       
' K' G: z8 {( y" l    Change in hardness (pts)        -10~+9
    Change in tensile (%)        -15 max
( U! B  j. [9 v% k" }6 `    Change in elongation (%)        -25 max
0 [# T" }) o' `7 U" Q    Change in volume (%)        -3~+10
# _+ [0 g! N" vOil Resistance ASTM#3 oil 160C@72hrs       
    Change in hardness (pts)        -10 max
    Change in tensile (%)        -15 max
    Change in elongation (%)        -15 max
    Change in volume (%)        10 max       
Compression set 160C@168hrs, %        25 max

chenhu

楼主你这个要用过氧的，HNBR压变，强度都很不错的，自己动手调两个配方，生胶的选择较为重要，用过氧硫化选择RDB残余双键含量低的，RDB越低越适合用过氧硫化的，RDB高的适合用S硫化。油不要用了，
具体就不详说，楼主自己先动手做一下，强度，选择N550或者并用少量N774，这样压变和强度都有保证，N330强度就好些压变差，N774呢压变好强度差，
自己动手多试试。

zhjlll1111

这个配方我用过氧化物做过了，压缩变形和伸长率有矛盾，另外耐NO.3油和耐转向油有矛盾啊

wilson_wx

把配方贴出来，大家给你点意见吧

njdt

耐油还好了，可以找到平衡点的，压变和伸长矛盾吗？

weizw55

保证了压变就保证不了伸长率吧.耐3号油也很难过.

weizw55

如果LZ能开发成功,且成本控制在160以内.我每月跟你拿500公斤.呵呵

weizw55

从技术要求上来看,像是宁国中鼎也开发过一样的产品.LZ是宁国的吧,何不去直接问问中鼎呢.呵呵....

我为胶狂

这个配方感觉有难度啊，期待高手解答 顶下