炭黑表面活性对填料网络和填料与橡胶之间相互作用的影响

labs

炭黑表面活性对填料网络和填料与橡胶之间相互作用的影响
9 x. m2 x6 M! O- H5 ~% y方亮 李秋影 许海燕 吴驰飞PDF

华东理工大学材料科学与工程学院高分子合金研究室,上海200237摘　要:采用原位固相接枝技术,将天然橡胶大分子接枝到炭黑表面,并考察了炭黑表面活性对其填充天然橡胶中填料网络和填料与橡胶相互作用程度的影响。结果表明：炭黑经过接枝改性后,其表面活性增加,且与橡胶基体的相互作用力增大,炭黑之间的网络化程度降低。[著者文摘]

关键词:炭黑 填料网络 Payne效应
  `" M" h; G2 Z& i分类号:　TQ330.3[著者标引]文献标识码：A文章编号：1006-3080（2008）05-0684-04栏目信息：材料科学与工程
相关文献:主题相关

- p  G& R# ]. x) `% dEffect of Surface Activity of Carbon Black on the Strength of Filler Network and Filler-Rubber InteractionFANG Liang, LI Qiu-ying, XU Hai-yan, WU Chi-fei Polymer Alloy Laboratory, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237, ChinaAbstract:Nature rubber was grafted on the surface of carbon black （CB） to modify the surface activity of CB via the in situ solid state grafting. Results of bound rubber showed that the surface activity of grafted CB was increased. Influences of the surface activity of CB on the strength of filler network and the filler-rubber interaction were investigated with rubber-process-analyzer （RPA） and dynamic mechanical analysis （DMA）. Results showed that compared with the system filled with original CB, the filler-rubber interaction was enhanced and the strength of filler network was decreased for the system filled with grafted CB.[著者文摘]

Key words:carbon black; filler network; Payne effect
/ ?6 L  y: u4 J  Z7 _/ ~; A# H
7 P' d) x: m( n) a6 M- _收稿日期:　2007-09-29修订日期:　基金资助:国家自然科学基金重点项目（50733001）
% Q8 ^  g0 r* v8 q8 Q5 m作者简介:方亮（1982-），男，浙江金华人，硕士研究生，主要研究炭黑的改性及应用。E-mail：shadow_12_19@yahoo．com．cn 通讯联系人：许海燕，E-mail：xuhaiyan@ecust．edu．cn

TGJ_777

优秀材料，好好学习！！！！！！！！

纳米郎

读书心得
本文属国内传统的研究方法
为了论文而论文的讨论
内容浅显 深度不够
可以当做初步读物，了解一下而已
8 {+ a* U# Y% F" n
推荐指数3 （为了发表论文而写的论文，浅显易懂，入门读物）