三元乙丙与硅胶共混问题请教!

adsiss

根据日本公司的胶种,本公司做红外光谱正在着手研究三元乙丙与硅胶的共混,目的是为了提高三元乙丙的耐热性能(190以上),配方体系中不能用硫磺硫化,因为气味比较大
现把客户的要求发布如下:
0 c: g# M- M1 f邵尔硬度:75+-5;
拉伸强度:>12MPa;
伸长率:200%-300%左右;
) m- }2 M3 I6 R# e" ]( V& r拉断永久变形:<4%
' q& `2 Z& {( Z  [25%压缩变形(150*72):<40%
9 m% Y: Q: h5 O; o" ]# G" c目前物性基本没问题,就是压变比较大,加工时容易分层
1 |- K3 f, ?' B) j+ s! ]) |* _在此请教各位有没有这方面的经验,或者对硅烷偶联剂比较有经验的方便介绍一下啊,非常感谢!

swrcc

直接用硅酮改质epdm如何?
8 x: ^) G7 x, P- ?3 w9 D1 `7 `
ROYALTHERM 1721 a modified EPDM with a special silicone rubber. ROYALTHERM is
5 j6 |' t6 ]4 [supplied as a base compound that can be vulcanized with peroxides or sulfur/accelerator
# F, E5 d% S, X: l+ Asystems. ROYALTHERM 1721 is 55 - 65 Durometer when vulcanized with 1.8 phr of dicumyl
- `" R' T1 o' A1 @peroxide. It can be blended with 1421 for intermediate hardness applications.
! y6 U1 s0 Z4 m! @% p2 T. MROYALTHERM 1721 is recommended for applications that require higher tensile strength than
' Q+ [7 F  s9 y1421. ROYALTHERM 1721 is also recommended for applications that require retention of
mechanical strength at elevated temperatures, weather and moisture resistance, electrical
% U! X  q! C- C. x0 bstability and compression recovery at low temperatures. It has superior overall heat resistance to
1711.

MDS

EPDM 与硅胶并用比较难！学习一下。

helong

用过氧化物硫化应该没问题。

metahjlf

是啊，我想还是用高门尼，配合炭黑好些，150不是太高

julun

关键混炼工艺是如何掌握，才能保证混炼胶的质量。

LionKing

建议用有机硅接枝EPDM，原美国康普顿的产品。

2楼是谁，居然找到一些英文的资料在这里贴？

周宏君

并用好像难些，不过楼主加油

hawk889

与我联系,大家想办法

陈工

几个方向：
1.用相容剂，有机硅改性EPDM有明显作用
3 Q8 I6 {* O2 v4 U$ P2.用共交联剂有一定作用，如PDM
3.自己用偶联剂预交联EPDM有效，实质就是做相容剂