误人子弟！Elongation is more than 400%. Who dare to use this compound to mold brake cup!. I have more than 16 years work with brake cup.

wenming0524 · 发表于 2008-5-5 04:36:26

孙正平

jwm700 · 发表于 2008-5-6 01:24:18

看看

Royalene · 发表于 2008-5-6 18:13:51

以下是引用 dmtyy 在 2008-5-4 17:49:20 的发言：
: w# U* c9 Q2 \3 b8 h! }! O# H误人子弟！Elongation is more than 400%. Who dare to use this compound to mold brake cup!. I have more than 16 years work with brake cup.

Hi, I'm glad to see that someone can talk out in different point of views.

However, why do you think EAB over 400% will not work for molded brake cup? The data are obtained on sample bars which cannot be absolutely used as a criteria to judge whether a formulation is suitable or not.

It is admirable that one can work on brake cup for over 16 years, yet longer history/experience never stands for being right always. Do you agree?